| Cyfansoddiad cemegol 17mn4 | |||||||
| Raddied | Yr elfen ar y mwyaf (%) | ||||||
| 17mn4 | C | Si | Mn | P | S | Han | Cr |
| 0.14-0.20 | 0.40 | 0.90-1.40 | 0.035 | 0.030 | 0.02 | 0.25 | |
| Cu | NI | Mo | Nb | Ti | V | ||
| 0.3 | 0.3 | 0.10 | 0.01 | 0.03 | 0.03 | ||
| Raddied | Eiddo mecanyddol 17mn4 | |
| Thrwch | Gnydi | |
| 17mn4 | mm | Min MPA |
| 6-16 | 290 | |
| 16-40 | 285 | |
| 40-60 | 280 | |
| 60-100 | 255 | |
| 100-150 | 230 | |
1. Pa brosesau trin gwres sydd eu hangen?
Ateb:
Prosesau Gweithgynhyrchu Safonol:
Normaleiddio (880-950°C) for thickness >30mm
Cyflwr wedi'i rolioam drwch yn llai na neu'n hafal i 30mm
Anelio Rhyddhad Straen Dewisol(580-620 gradd)
Proses Rheoli Thermomecanyddol (TMCP)Ar gael ar gyfer gwell eiddo
2. Pa weithdrefnau weldio sy'n cael eu hargymell ar gyfer 17mn4?
Ateb:
Arferion weldio hanfodol:
Rhagboethasit: 100-150°C (for t>25mm)
Nwyddau traul: Din 8556 e 42 4 b 42 neu gyfwerth
Mewnbwn gwres: 1.8-3.2 kJ/mm
Tymheredd Interpass: Llai na neu'n hafal i 250 gradd
Triniaeth Gwres ar ôl (PWHT): 580-620°C × 1hr/25mm (for t>35mm)
3. Ble mae 17mn4 wedi'i nodi'n nodweddiadol?
Ateb:
Ymhlith y ceisiadau cyffredin mae:
Cychod Canolig-Pwysedd(10-40 bar)
Drymiau a phenawdau boeler
Cregyn cyfnewidydd gwres
Prosesu offer mewn planhigion cemegol
Tanciau storio at ddefnydd diwydiannol
Cymhariaeth â graddau tebyg
| Raddied | Safonol | Cryfder Cynnyrch | Gwahaniaeth allweddol |
|---|---|---|---|
| 17mn4 | DIN 17155 | Yn fwy na neu'n hafal i 355 MPa | Safon Almaeneg gyda chynnwys MN wedi'i optimeiddio |
| P355GH | EN 10028-2 | Yn fwy na neu'n hafal i 355 MPa | Cyfwerth Ewropeaidd |
| A516 gr.70 | ASTM | Yn fwy na neu'n hafal i 260 MPa | Safon yr UD, Cryfder Cynnyrch Is |
Tagiau poblogaidd: DIN 17155 17 mn4 ar gyfer plât llestr pwysau, China din 17155 17 mn4 ar gyfer gweithgynhyrchwyr plât cychod pwysau, cyflenwyr, ffatri