A516Gr70+316L Plât dur cladin Cyfansoddiad Cemegol ac Eiddo Mecanyddol
|
ASTM A516 Gradd 70 Cyfansoddiad Cemegol |
|||||
|
Gradd |
Yr Elfen Max (%) |
||||
|
C |
Si |
Mn |
P |
S |
|
|
ASTM A516 gradd 70 |
|||||
|
Trwchus<12.5mm |
0.27 uchafswm |
0.15–0.40 |
0.85–1.20 |
0.035 |
0.035 |
|
Trwchus 12.5-50mm |
0.27 uchafswm |
0.15–0.40 |
0.85–1.20 |
0.035 |
0.035 |
|
Trwch 50-100mm |
0.27 uchafswm |
0.15–0.40 |
0.85–1.20 |
0.035 |
0.035 |
|
Trwchus 100-200mm |
0.27 uchafswm |
0.15–0.40 |
0.85–1.20 |
0.035 |
0.035 |
|
Thick>200mm |
0.27 uchafswm |
0.15–0.40 |
0.85–1.20 |
0.035 |
0.035 |
|
Elfen |
Canran (%) |
|
carbon (C) |
0.27 uchafswm |
|
Manganîs (Mn) |
0.85–1.20 |
|
Ffosfforws (P) |
0.035 uchafswm |
|
sylffwr (S) |
0.035 uchafswm |
|
silicon (Si) |
0.15–0.40 |
|
Nicel (Ni) |
0.40 uchafswm (dewisol) |
|
Cromiwm (Cr) |
0.30 uchafswm (dewisol) |
|
molybdenwm (Mo) |
0.08 uchafswm (dewisol) |
|
Gradd |
ASTM A516 Gradd 70Eiddo Mecanyddol |
|||
|
Trwch |
Cnwd |
Tynnol |
Elongation |
|
|
ASTM A516 gradd 70 |
mm |
Mpa Isaf |
Mpa |
Isafswm % |
|
6-40 |
260 |
485-620 |
21% |
|
|
40-100 |
260 |
485-620 |
17% |
|
| Gradd |
C
|
Mn |
P
|
S
|
Si |
Cr |
Ni | Mo | Ni |
Cooper
|
| 316L(S31603) | 0.030 | 2.0 | 0.045 | 0.030 | 0.75 | 16.0-18.0 | 10.0-14.0 | 2.00-3.00 | 0.10 | - |
| Gradd |
Cryfder cynnyrch (N/mm2), mun |
Cryfder tynnol (N/mm2), min |
Elongation mewn 2 modfedd (50mm), %, min |
|
Tro oer | ||||||
|
Austenitig (Cromiwm-nicel) (Cromium-Manganîs-Nicel) |
|||||||||||
| 316L(S31603) |
|
|
40 |
|
ddim yn ofynnol | ||||||
A516Gr70+316L Cymhwysiad Plât dur Clad
Diwydiant Cemegol:
Tanciau Storio Asid: Gwrthsefyll 5–20% o asid sylffwrig a-dŵr gwastraff llawn clorid.
Adweithyddion: Trin synthesis organig o dan bwysau a thymheredd uchel.
Olew a Nwy:
Unedau Hydrocracio: Mae A516Gr70 yn darparu cyfanrwydd strwythurol, tra bod 316L yn gwrthsefyll H₂S a chorydiad clorid.
Piblinellau Tanfor: Gwrthsefyll dŵr môr a hylifau hydrocarbon pwysedd uchel.
Peirianneg Forol:
Gweithfeydd Dihalwyno: Gwrthsefyll diheintyddion sy'n seiliedig ar ddŵr hallt a chlorin.
Tanciau Bwrdd Llongau: Storiwch danwydd neu ddŵr môr heb fawr o gyrydiad.
Bwyd a Fferyllol:
Offer Prosesu: Cwrdd â safonau'r FDA ar gyfer hylendid (Ra Llai na neu'n hafal i 1.6μm) a gwrthsefyll asiantau glanhau.
A516Gr70+316L Plât dur cladin Enw Arall
A516Gr70+316L Plât dur cladin, plât dur A516Gr70, plât dur 316L
Arloesedd Technolegol O Dan Amodau Gwaith Arbennig
Weldio mewn-Amgylcheddau Tymheredd Isel
Pan fydd y tymheredd amgylchynol<0°C, additional preheating to 200–250°C is required, and the "multi-layer and multi-pass welding" method should be adopted, with the interpass temperature maintained at 150–200°C.
Dylid cynnal gwresogi post (250-300 gradd, dal am 1 awr) yn syth ar ôl weldio i gyflymu trylediad hydrogen.
Amddiffyniad yn Erbyn Cyfryngau Cyrydol Iawn
Transition Layer Upgrade: In environments with Cl⁻ concentration >1000ppm, argymhellir defnyddio ER NiCrMo-3 (Inconel 625) ar gyfer yr haen bontio, sy'n cynnwys 9-10% Mo ac sydd â Rhif Cyfwerth â Gwrthsefyll Pitting (PREN) Mwy na neu'n hafal i 40.
Gorchuddio Arwyneb: Ar ôl weldio, mae wyneb yr haen cladin yn cael ei chwistrellu â gorchudd cyfansawdd resin epocsi / alwmina (trwch 150-200μm). Mae'r amser ymwrthedd cyrydiad yn y prawf chwistrellu halen (ASTM B117) yn fwy na 5000 awr.
Ar gyfer llestri pwysedd glanweithiol mewn diwydiannau fferyllol/bwyd (ee, tanciau storio cyffuriau di-haint, offer prosesu llaeth), rydym yn darparu Q345B+304L Clad steel neu Q235B+304 Clad steel sy'n bodloni safonau gradd TSG 21 a bwyd-. Os oes angen i chi wybod gofynion garwedd wyneb, weldadwyedd gyda ffitiadau misglwyf, neu gyfrifo costau prosesu ar gyfer ceudodau mewnol wedi'u haddasu, anfonwch ymholiad ar gyfer dogfennau ymgynghori ac ardystio proffesiynol.